焊缝金属分析
Mn | |||
Mn | C | Si | Cr |
0.7 % | - | - | - |
C | |||
Mn | C | Si | Cr |
- | 0.67 % | - | - |
Si | |||
Mn | C | Si | Cr |
- | - | 0.7 % | - |
Cr | |||
Mn | C | Si | Cr |
- | - | - | 10.4 % |
熔敷数据
Fusion time per electrode at 90% I max | kg weld metal/kg electrodes | Number of electrodes/kg weld metal | 安培 | 熔敷率 | 电压 V | 直径 |
62 sec | 0.67 kg | 58 | 75-110 A | 1.0 kg/h | 23 V | 2.5 x 350 mm |
95 sec | 0.67 kg | 27 | 110-150 A | 1.4 kg/h | 23 V | 3.2 x 450 mm |
107 sec | 0.67 kg | 18 | 145-200 A | 1.9 kg/h | 24 V | 4.0 x 450 mm |
110 sec | 0.66 kg | 12 | 190-270 A | 2.8 kg/h | 26 V | 5.0 x 450 mm |