Typical Tensile Properties
As welded | |||
保护气体 | Elongation | Tensile Strength | Yield Strength |
ISO | - | - | - |
AWS | 22 % | 570 MPa | 480 MPa |
夏比V型缺口冲击性能
As welded | ||
Testing Temperature | 保护气体 | Impact Value |
-20 °C | ISO | - |
-20 °C | AWS | 55 J |
-30 °C | AWS | 45 J |
焊缝金属分析
Mn | ||||
Mn | Mo | C | Si | Ni |
0.46 % | - | - | - | - |
Mo | ||||
Mn | Mo | C | Si | Ni |
- | 0.24 % | - | - | - |
C | ||||
Mn | Mo | C | Si | Ni |
- | - | 0.09 % | - | - |
Si | ||||
Mn | Mo | C | Si | Ni |
- | - | - | 0.12 % | - |
Ni | ||||
Mn | Mo | C | Si | Ni |
- | - | - | - | 0.34 % |
熔敷数据
Fusion time per electrode at 90% I max | kg weld metal/kg electrodes | Number of electrodes/kg weld metal | 安培 | 熔敷率 | 电压 V | 直径 |
90 sec | 0.58 kg | 65 | 65-120 A | 0.62 kg/h | 31 V | 3.2 x 350 mm |
93 sec | 0.59 kg | 42 | 90-180 A | 0.93 kg/h | 30.5 V | 4.0 x 350 mm |
100 sec | 0.67 kg | 24 | 150-240 A | 1.47 kg/h | 28.6 V | 5.0 x 350 mm |